Zheflon® FL2606 Copolymer PVDF - Extrusion Grade

Zheflon® FL2606 Copolymer PVDF - Extrusion Grade
Zheflon® FL2606 Copolymer PVDF - Extrusion GradeZheflon® FL2606 Copolymer PVDF - Extrusion GradeZheflon® FL2606 Copolymer PVDF - Extrusion Grade

Zheflon® FL2606 Copolymer PVDF - Extrusion Grade

Zheflon®FL2606 PVDF copolymer is medium and low viscosity grade that with high purity.
产品目录PVDF for Lithium Batteries
品牌孚诺林
产品规格FL2606
FeaturesCopolymer, Medium and low viscosity
UsesWire&cables, Extruded pipe, Bar, Plate, Wire&cable
FormsTranslucent white particles
ProcessingSuspension PVDF
更新时间2024/4/17
详细信息

Zheflon®FL2606 PVDF copolymer is medium and low viscosity grade that with high purity. Important properties include excellent chemical resistance to most aggressive substances and solvents, excellent mechanical strength and toughness, high abrasion resistance, high temperature capabilities, excellent aging resistance, low permeability to most gases and liquids and easily melt-processed by standard methods of extrusion.

General

Features

Copolymer, Medium and low viscosity

Uses

Extruded pipe, Bar, Plate, Wire&cable

Forms

Translucent white particles

Items

Typical Value FL2606

Test Method

Physical Properties

Density(g/cc)

1.77~1.80

ASTM D792

Melt Flow Rate(g/10min)

4.0~8.0

Load 5kg, 230℃,ASTM D1238

Melt viscosity(Kps)

10~15

Shear Rate 100 1/s, ASTM D3835

 

Water Absorption(%)(Time 24 hr)

≤0.040

ISO 62

Linear Mold Shrinkage(cm/cm)

0.0200~0.0300

 

Molecular Properties

Molecular weight(Da)

350,000~440,000

GPC,DMF,ISO 16014

Intrinsic viscosity(dl/g)

1.10~1.30

30℃,DMAC

Molecular weight distribution

2.0-3.0

GPC,DMF,ISO 16014

Mechanical Properties

Tensile Modulus(Thickness2.00mm)(MPa)

800~1200

1.0mm/min,ASTM D638

Flexural Modulus(Thickness2.00mm)(MPa)

700~1000

2.0mm/min,ASTM D790

Yield Strength(Thickness2.00mm)(MPa)

30.0~40.0

50mm/min,ASTM D638

Break Strength(Thickness2.00mm)(MPa)

20.0~35.0

50mm/min,ASTM D638

Elongation at Yield(%)

10.0~15

50mm/min,ASTM D638

Elongation at Break(%)

200~600

50mm/min,ASTM D638

Hardness, Shore D(Thickness2.00mm)

70~75

ASTM D2240

Izod Impact, Notched(Thickness 4.00mm, 23℃)(J/m)

150~200

Notched V 10 mm

ASTM D256

Thermal Properties

Melting Point(℃)

158~166

ASTM D3418

Crystallization Temperature(DSC peak)(℃)

115~130

ASTM D3418

Glass Transition Temp, Tg(℃)

-32.0

ASTM E1356

Decomposition Temperature(℃)

330~350

1% wt. loss / in air

Vicat Softening Point(℃)

90~105

ASTM D1525

Heat deflection temperature at 1.8 MPa(Thickness 4.00mm)(℃)

50~60

After annealing 150℃,16h

ASTM D648

Electrical Properties

Surface Resistance(ohm)

≥1.00E+14

Voltage<1V,After 2 min—500V

ASTM D257

Electrical Resistivity(ohm·cm)

≥1.00E+14

Intensity=10mA,After 2 min@23℃

ASTM D257

Dielectric strength(Thickness 1.00mm,23℃)(KV/mm)

20~25

ASTM D149

Dielectric constant(1kHz,23℃)

7.0~10.0

ASTM D150

Burning Properties

UL Flame retardant grade(0.100mm)

V-0

UL94

Oxygen Index(3.00mm)

44%

ASTM D2683


1.PVDF should be processed under 260℃,to avoid producing toxic gases;

2.PVDF has good fire resistance and smoke inhibition property, however, when meets with fire, it will release toxic hydrogen fluoride gas and fluorocarbon compounds;

3.Operators should take good care of personal protection during the use procedure and processing.


PVDF is packed in PE plastic bag and then be put into a drum with the net weight 25KGS. It must be stored in clean, cool, dry place.